Analisa perbandingan kekuatan hasil pengelasan TIG dan pengelasan MIG pada Aluminium 5083

Iswanto Iswanto, Noerdianto Noerdianto, A’rasy Fachruddin, Mulyadi Mulyadi

Abstract


This paper will discuss the comparative strength of TIG (Tungsten Inert Gas) welding results and MIG (Metal Inert Gas) welding results. Welding is carried out on aluminium material 5083, by varying the amount of amperage in each type of welding. Amperes variations used in TIG welding and MIG welding are 130 Amperes, 140 Amperes , and 150 Amperes. Furthermore, testing is carried out to determine the strength of the welding results, namely by bending and tensile test. From the bending test results obtained the highest bending strength of 262.36 kgf/mm2, obtained at MIG welding with a strong current used 130 Amperes. The lowest bending strength of 21.61 kgf/mm2, is obtained in TIG welding with the strong current used by 130 Amperes. From the tensile test results obtained the highest tensile strength of 23.48 kgf/mm2, obtained at MIG welding with a strong current used 130 Amperes. The lowest tensile strength of 17.41 kgf/mm2, obtained at TIG welding with a strong current used 130 Amperes.
Keywords: TIG welding, MIG welding, Aluminium 5083.


Full Text:

PDF

References


. Dewanto, A.P. dkk., 2016. Analisa kukuatan mekanik sambungan las metode MIG (metal inert gas) dan metode FSW (friction stir welding) 800 rpm pada Aluminium tipe 5083. Jurnal Teknik Perkapalan. vol. 4, no. 3, hal. 613-631.

. Kou, Sindo, 2003. Welding Metallurgy, 2nd Ed., A John Wiley & Sons, Inc., New Jersey, Canada.

. Syahrani, A. Dkk., 2017. Pengaruh variasi arus pengelasan GTAW terhadap sifat mekanis pada pipa baja karbon ASTM A 106. Jurnal Mekanikal. vol. 8, no.1, hal. 721- 729.

. Informasi dari https://www.weldingis.com/gtaw-welding/ (diakses pada 30 Maret 2020)

. Mathers Gene, 2002. The Welding of Aluminium and its alloys, CRC Press, Washington.

. Darsin, M. Dkk., 2010. Analisa sifat mekanik dan struktur mikro paduan Aluminium 5083 akibat pengelasan metal inert gas (MIG) dengan variasi preheat dan post heat. Jurnal ROTOR. vol. 3, no. 2, hal. 67-74.

. Naharuddin, Dkk., 2015. Kekuatan tarik dan bending sambungan las pada material baja SM 490 dengan metode pengelasan SMAW dan SAW. Jurnal Mekanikal. vol. 6, no. 1, hal. 551-555.

. Hermanto, Aris dan Iswanto, 2018. Pengaruh flux elektroda AWS 5.1 E 6013 dicelup oli pada pengelasan besi cor kelabu FC-25 terhadap kekuatan tarik. Jurnal REM. vol. 3, no. 2, hal. 57-60.

. Budiyanto, E., Nugroho, E., & Masruri, A. (2017). Pengaruh diameter filler dan arus pada pengelasan TIG terhadap kekuatan tarik dan struktur mikro pada baja karbon rendah. Turbo: Jurnal Program Studi Teknik Mesin, 6(1).




DOI: http://dx.doi.org/10.24127/trb.v9i1.1166

Refbacks

  • There are currently no refbacks.